Издательство СО РАН

Издательство СО РАН

Адрес Издательства СО РАН: Россия, 630090, а/я 187
Новосибирск, Морской пр., 2

soran2.gif

Baner_Nauka_Sibiri.jpg


Яндекс.Метрика

Array
(
    [SESS_AUTH] => Array
        (
            [POLICY] => Array
                (
                    [SESSION_TIMEOUT] => 24
                    [SESSION_IP_MASK] => 0.0.0.0
                    [MAX_STORE_NUM] => 10
                    [STORE_IP_MASK] => 0.0.0.0
                    [STORE_TIMEOUT] => 525600
                    [CHECKWORD_TIMEOUT] => 525600
                    [PASSWORD_LENGTH] => 6
                    [PASSWORD_UPPERCASE] => N
                    [PASSWORD_LOWERCASE] => N
                    [PASSWORD_DIGITS] => N
                    [PASSWORD_PUNCTUATION] => N
                    [LOGIN_ATTEMPTS] => 0
                    [PASSWORD_REQUIREMENTS] => Пароль должен быть не менее 6 символов длиной.
                )

        )

    [SESS_IP] => 18.209.69.180
    [SESS_TIME] => 1711697497
    [BX_SESSION_SIGN] => 9b3eeb12a31176bf2731c6c072271eb6
    [fixed_session_id] => b25d2c01de1726de1ad12a0df6bedd62
    [UNIQUE_KEY] => ea3844c0b30c1c492e7d32314ec24cbc
    [BX_LOGIN_NEED_CAPTCHA_LOGIN] => Array
        (
            [LOGIN] => 
            [POLICY_ATTEMPTS] => 0
        )

)

Поиск по журналу

Химия в интересах устойчивого развития

2005 год, номер 2

Solid-State Synthesis of Cost-Efficient Powder Filler Metals for Vacuum Brazing of Titanium Alloys

E. YU. Ivanov and A. E. Shapiro
1Tosoh SMD Inc., 3600 Gantz Rd., Grove City, Ohio (USA), E-mail: eugene.ivanov@tsmd.com
2Titanium Brazing, Inc., Columbus, Ohio (USA)
Страницы: 205-208

Аннотация

Titanium alloys are typically brazed in the USA and Russia with two powder filler metals of Ticuni® family having compositions of 70Ti-15Cu-15Ni and 60Ti-15Cu-25Ni, several pre-alloyed filler metals of Ti-Zr-Cu-Ni system such as VPr16 and VPr28 powders, and amorphous foils of Stemet® family. All these brazing materials are characterized by high price that may be attributed to both the cost of the components and atomization process of Ti- and Zr-based alloys or with the production of amorphous tapes.
The technology of producing mechanically-alloyed filler metals from elemental metal powders or hydrides was developed to cut manufacturing expenses by 40-50%. Some of these alloys such as TiBraze®375 (Ti-37.5Zr-15Cu-10Ni), TiBraze®260 (Ti-26Zr-14Cu-14Ni-0.5Mo), and TiBraze®15-15 (Ti-15Cu-15Ni) were successfully tested and accepted by the USA industry. These mechanically-alloyed filler metals are characterized by low erosion of base materials, tensile strength of Ti-6Al-4V brazed joints in the range of 670-740 MPa depending on the brazing gap and temperature, shear strength of joints 520-580 MPa, and by relatively low brazing temperature in the range of 850-890oC that allows to perform the brazing process below -transus temperature of most titanium base alloys. Solid-state synthesis of Ti-Zr-Cu-Ni alloys was investigated by varying the time of high-energy ball milling. The products were studied by DTA, EDS analysis, and scanning electron microscopy. Clear evidences of solid-state reactions obtained in this study confirm that the resulting alloys are partially pre-alloyed and comprise Cu and Ni dispersed throughout the Ti and Zr phases. DTA results displayed a decrease in the liquidus temperature. The notable effect of milling is the induced exothermic effect prior to melting of mechanically-alloyed brazing alloys.