Издательство СО РАН

Издательство СО РАН

Адрес Издательства СО РАН: Россия, 630090, а/я 187
Новосибирск, Морской пр., 2

soran2.gif

Baner_Nauka_Sibiri.jpg


Яндекс.Метрика

Array
(
    [SESS_AUTH] => Array
        (
            [POLICY] => Array
                (
                    [SESSION_TIMEOUT] => 24
                    [SESSION_IP_MASK] => 0.0.0.0
                    [MAX_STORE_NUM] => 10
                    [STORE_IP_MASK] => 0.0.0.0
                    [STORE_TIMEOUT] => 525600
                    [CHECKWORD_TIMEOUT] => 525600
                    [PASSWORD_LENGTH] => 6
                    [PASSWORD_UPPERCASE] => N
                    [PASSWORD_LOWERCASE] => N
                    [PASSWORD_DIGITS] => N
                    [PASSWORD_PUNCTUATION] => N
                    [LOGIN_ATTEMPTS] => 0
                    [PASSWORD_REQUIREMENTS] => Пароль должен быть не менее 6 символов длиной.
                )

        )

    [SESS_IP] => 3.238.161.165
    [SESS_TIME] => 1711652345
    [BX_SESSION_SIGN] => 9b3eeb12a31176bf2731c6c072271eb6
    [fixed_session_id] => 202dbc908a6b4c066cfd873209df0fa8
    [UNIQUE_KEY] => 75bafce42eb9f155c94c634c4c5de461
    [BX_LOGIN_NEED_CAPTCHA_LOGIN] => Array
        (
            [LOGIN] => 
            [POLICY_ATTEMPTS] => 0
        )

)

Поиск по журналу

Журнал структурной химии

2011 год, номер 2

STRUCTURE, THERMAL STABILITY, AND CATALYTIC PERFORMANCE OF MgO-ZrO2 COMPOSITES

T. ??valos-rend??n1, J. Ort??z-landeros1, G. Fetter2, V.H. Lara3, P. Bosch1, H. Pfeiffer1
1 Instituto de Investigaciones en Materiales
2 Facultad de Ciencias Química, Universidad Autónoma de Puebla
3 Departamento de Química Universidad Autónoma Metropolitana-Iztapalapa
Ключевые слова: catalyst supports, ceramic-matrix composites (CMCs), thermal properties, thermal analysis, zirconia
Страницы: 349-357

Аннотация

A composite constituted by zirconia supported on magnesia is thermally treated. Depending on temperature, several crystal sizes and crystalline zirconia structures are obtained. At low temperatures, cubic zirconia crystals are found to be deposited on the crystalline magnesia matrix. As temperature increases, the cubic zirconia phase transforms to the tetragonal and the monoclinic phases. They form clusters supported on the MgO matrix. All these results are supported by different analytical techniques and a catalytic test.